疲劳、断裂相关试验标准总结1. 金属材料疲劳、断裂试验标准方法1.1 ASTM 相关标准ASTM E739 线性或线性化应力-寿命（S-N）和应变- 寿命（e-N）ASTM E647 疲劳裂纹扩展速率试验方法ASTM E468 Standard Practice for Presentation of Constant Amplitude Fatigue Test Results for Metallic MaterialsASTM E466 金属材料力控制恒幅轴向疲劳试验方法ASTM E399 Standard Test Method for Linear-Elastic Plane-Strain Fracture Toughness of Metallic MaterialKASTM E561 Standard Test Method for K-R Curve DeterminationASTM E740 Standard Practice for Fracture Testing with Surface-Crack Tension SpecimensASTM E1152 Standard Test Method for determining J-R CurvesASTM E1820 Standard Test Method for Measurement of Fracture ToughnessASTM E606/E606M Standard Test Method for Strain-Controlled Fatigue TestingASTM E1942 Standard Guide for Evaluating Data Acquisition Systems Used in Cyclic Fatigue and Fracture Mechanics TestingASTM E2472 Standard Test Method for Determination of Resistance to Stable Crack Extension under Low-Constraint ConditionsASTM B646 Standard Practice for Fracture Toughness Testing of Aluminum AlloysASTM E2818 Standard Practice for Determination of Quasistatic Fracture Toughness of Welds1.2 GB 相关标准GB/T 3075 金属轴向疲劳试验方法GB/T 6398 金属材料 裂纹扩展试验方法GB/T 4337 金属旋转弯曲疲劳试验方法 GB/T 7733 金属旋转弯曲腐蚀疲劳试验方法GB/T 12443 金属扭应力疲劳试验方法GB/T 7732 金属材料 表面裂纹拉伸试样断裂韧度试验方法GB/T 21143 金属材料 准静态断裂韧度的统一试验方法GB/T 24176 金属材料 疲劳试验数据统计方案与分析方法GB/T 2107 金属高温旋转弯曲疲劳试验方法GB/T15248 金属材料 轴向等幅低循环疲劳试验方法GB/T10622 金属材料 滚动接触疲劳试验方GB/T 4161 金属材料平面应变断裂韧度 试验方法KGB/T 2038 金属材料延性断裂韧度 试验方法GB/T 26077 金属材料疲劳试验轴向应变控制方法GB/T 26076 金属薄板（带）轴向力控制疲劳试验方法GB/T 27595 胶粘剂结构胶粘剂拉伸剪切疲劳性能的试验方法GB/T 12443 金属材料扭应力疲劳试验方法GB/T 13682 螺纹紧固件轴向疲劳试验方法GB/T 30064 金属材料 钢构件断裂评估中裂纹尖端张开位移(CTOD)断裂韧度的拘束损失修正方法GB/T 24522 金属材料 低拘束试样测定稳定裂纹扩展阻力的试验方法GB/T 28896 金属材料 焊接接头准静态断裂韧度测定的试验方法GB/T 27551 金属材料焊缝破坏性试验 断裂试验 1.3 HB 相关标准HB 5142 金属材料平面应变断裂韧度 试验方法KHB 5152 金属室温旋转弯曲疲劳试验方法HB 5153 金属高温旋转弯曲疲劳试验方法HB 5217 金属低周热疲劳试验方法HB 5277 发动机叶平及材料振动疲劳试验方法HB 5287 金属材料轴向加载疲劳试验方法HB 5279 金属板材表面裂纹断裂韧性试验方法HB 5487 铝合金断裂韧度试验方法HB 6626 金属材料在含水介质中疲劳裂纹扩展速率试验方法HB 7572 金属材料（人字形缺口）平面应变断裂韧度试验方法HB 7680 金属材料高温疲劳裂纹扩展速率试验方法HB 7705 金属材料疲劳小裂纹扩展速率试验方法HB 6442 飞机液压导管及连接件弯曲疲劳试验HB 7680 高温疲劳裂纹扩展速率试验方法HB 5261 金属板材 K-R 曲线试验方法HB 6660 金属板材热疲劳试验方法HB 7110 金属材料细节疲劳额定强度截止值（DFRcutoff）试验方法HB/Z 112 材料疲劳试验统计分析方法HB 20041 航空发动机轴类部件疲劳试验方法1.4 GJB 相关标准GJB 2030 高温下金属材料断裂韧度 试验方法GJB 1997 金属材料轴向腐蚀疲劳试验方法GJB 715.30A 紧固件试验方法-拉伸疲劳GJB 715.30 紧固件试验方法-抗拉疲劳GJB 715.9 紧固件试验方法-抗剪接头疲劳2. 复合材料疲劳、断裂试验标准方法2.1 ASTM 相关标准ASTM D5528 Standard Test Method for Mode I Interlaminar Fracture Toughness of Unidirectional Fiber-Reinforced Polymer Matrix CompositesASTM D3479/D3479M Standard Test Method for Tension-Tension Fatigue of Polymer Matrix Composite MaterialsASTM D7774 Standard Test Method for Flexural Fatigue Properties of PlasticsASTM D7791 Standard Test Method for Uniaxial Fatigue Properties of PlasticsASTM D4482 Standard Test Method for Rubber Property-Extension Cycling FatigueASTM D7615/D7615M Standard Practice for Open-Hole Fatigue Response of Polymer Matrix Composite LaminatesASTM D3166 Standard Test Method for Fatigue Properties of Adhesives in Shear by Tension Loading (Metal/Metal)ASTM D6115 Standard Test Method for Mode I Fatigue Delamination Growth Onset of Unidirectional Fiber-Reinforced Polymer Matrix CompositesASTM E1049 Standard Practices for Cycle Counting in Fatigue Analysis2.2 GB 相关标准GB/T 16779 纤维增强塑料层合板 拉-拉疲劳性能试验方法GB/T 28891-2012 纤维增强塑料复合材料 单向增强材料型层间断裂韧性的测定2.3 HB 相关标准HB 7624 碳纤维复合材料层合板弯曲疲劳试验方法HB 5268 有机玻璃板材断裂韧度试验方法HB 7402 碳纤维复合材料层合板 I 型层间断裂韧性 试验方法HB 7403 碳纤维复合材料层合板 II 型层间断裂韧性 试验方法HB 7718.1 碳纤维复合材料层合板湿热环境下层间断裂韧性试验方法第 1 部分：I 型层间断裂韧性试验方法HB 7718.2 碳纤维复合材料层合板湿热环境下层间断裂韧性试验方法第 2 部分：II 型层间断裂韧性试验方法2.4 GJB 相关标准GJB 586 纤维增强塑料层板拉伸层间断裂韧性试验方法GJB 2637 碳纤维树脂基复合材料层合板疲劳试验方法GJB 2033 航空有机玻璃拉伸疲劳试验方法