大连交通大学2015届本科毕业设计（论文）摘 要 焊条电弧焊是药皮焊条手工电弧焊的简称。是用手工操纵焊条进行焊接的电弧焊方法。由于焊条电弧焊设备简单、操作灵活、可焊金属材料广等特点。焊条电弧焊主要用于焊接装配要求不高、结构复杂的单件或小批量的产品。本课题为了研究球墨铸铁与Q235普通碳素结构钢的焊接性，我们采用焊条电弧焊的这种工艺方法，采用不同的焊接材料进行焊接。试件焊接完成后，观察试件的焊缝成型，确认焊缝不具有错边、咬边、余高过高等外部缺陷。然后对试件进行切割观察内部缺陷如裂纹、未熔合等。对试件还要进行相应的拉伸试验以及金相组织观察，来验证焊缝是否达到相应的性能要求，以H08为焊芯钛钙型结构钢焊条J422、以镍铁合金为主要的成分的铸铁焊条Z408以及新型特种铸铁焊条WE777。实验结果表明：新型焊条WE777和铸铁焊条Z408的工艺性能和使用性能明显优于结构钢焊条J422。在实验过程中使用结构钢焊条的试件出现了明显的裂纹，无法达到相应的性能标准。另外在使用焊条电弧焊进行试件焊接过程中，特别容易出现夹杂等焊接缺陷。同时，有实验证明新型材料WE777在焊缝成型以及焊缝力学性能方面较铸铁焊条Z408好。由此证明，在球墨铸铁与Q235异种金属材料焊接过程中，在采用相同的焊接方法的前提下，使用合理的焊接材料以及焊接过程中正确的焊接流程，是至关重要的。关键词：焊条电弧焊 球墨铸铁 Q235 金相组织 焊接缺陷ABSTRACT Welding electrodeis theelectrodemanual electric arc weldingshort.Electric arc weldingmethod of weldingis carried outbymanual manipulation of electrode.Because theelectrode arc weldingequipment is simple,flexible operation,the characteristics ofweld metal materialsetc.Arc weldingis mainly used for weldingassembly requirementsis not high,the complex structure of thesingle or small batchproducts.This topicin order to study the weldabilityof nodular cast iron andQ235plain carbon structuralsteel,We use thismethod forshielded metal arc weldingprocess,Usingdifferent welding materialswelding.After the completion of weldingspecimen,Observe thetestweldmoulding,Weld is notwiththe wrong side,undercut,overhighhigherexternaldefects confirmation.Then thespecimenswere observed in internaldefects such ascracks,lack of fusionetc.The specimenalsocorrespondingtensile testand microstructure observation,To verifywhether meet the requirementsof correspondingproperties ofweld.This topic usesthree different types ofweldingmaterials is thatTaking H08 as thecoreof titanium calcium typestructural steel welding rodJ422,nickel iron alloyas the maincomponent ofcast iron welding rodZ408 andnew special type ofcast iron welding rodWE777.The experimental results show that theThe new electrodeWE777 andelectrode for cast ironZ408process performance and useperformance superior to that ofstructural steel electrodeJ422,Structural steel welding rodspecimensusedin the experimental processappearedobvious cracks,unable to reach thecorresponding performance criteria.In addition to the useof SMAWspecimensin the process of welding,especially prone toinclusionof welding defects.At the same time,experiments have proved thatthe new material WE777in theformation of weldand weldmechanical properties ofcast iron electrodeZ408 This proves that,in the weldingof ductile cast ironand Q235 dissimilar metalmaterials in the process ofusing,in thepremiseof the sameweldingmethod,weldingprocessthe rightwelding materialuseand reasonablewelding process,is essential.Key words: Arc welding Nodular cast iron Q235 Metallographicorganization Welding defects目 录第一章 绪论.11.1 铸铁.11.2 球墨铸铁.11.3 碳素结构钢.21.4 球墨铸铁与Q235钢焊接性分析.3 1.4.1 Q235普通碳素结构钢焊接性分析.4 1.4.2 球墨铸铁焊接性分析.4 1.4.3 球墨铸铁与Q235焊接的主要问题以及解决方案 .51.5 焊接方法及焊接材料.61.6 国内外研究状况.91.7 本课题研究的主要内容和意义.9第二章 实验材料及实验方法.102.1 实验材料.102.2 实验方法.10 2.2.1 试件焊前准备.10 2.2.2 球墨铸铁与Q235钢板施焊方法 .11 2.2.3 微观组织观察.12 2.2.4 试件拉伸实验.13 2.2.5 接头硬度实验.13第三章 实验结果及分析.143.1 碳钢焊条所焊试件开裂原因及分析.143.2 焊缝成型观察 .143.3 焊接接头显微组织微观结构观察分析.153.4 焊接接头抗拉强度试验结果分析.203.5 焊接接头硬度测量试验的结果分析.21第四章 结论.23谢辞.24参考文献.25第一章 绪论1.1 铸铁 铸铁是一种以碳、铁、硅为主要成分且在结晶过程中具有共析转变的多元铁基合金。碳在铸铁中既可以以化合态的渗碳体（Fe3C）形式存在，也可以以游离状态的石墨（G）形式存在。根据碳在铸铁中的存在状态和形式不同，可以将铸铁分为五类1。 （1）白口铸铁。 碳在铁中绝大部分以渗碳体（Fe3C）形式存在，因其断口成白色而得名。渗碳体的硬而脆、硬度为800HBS。因无法机械加工，所以应用不广，主要用于轧辊或其他不需要机械加工的耐磨零件。 （2）灰铸铁。 碳以片状石墨存在，因其端口成灰色而得名。普通灰铸铁中石墨片状较粗，如果在浇注